ALU-METAL spatula

ALU-METAL spatula

Product info:

Special spatula with aluminum pigments enables high Füllkraft.

• Very good adhesion to metal (iron, steel, aluminum), wood, stone and various plastics (eg rigid PVC, polyester) is also at higher temperatures (up to about 100 ° C)
• High filling and state property; there are large layer thicknesses up to 5 mm, or small layer thicknesses up to 10 mm in one operation, including possible 
• Good Ductility by creamy consistency 
• Rapid hardening (10-15 minutes) 
• Slight tear and high abrasion 
• Resistant to water, fuel, mineral oils, dilute acids and alkalis.

Applications:

• Aluminum metal spatula is mainly used in car body repair shops in the truck or engineering firms to Equalize of Ver-deepening rough or uneven application. He still finds application in other areas hobby as well as the bonding of mechanically not to be highly stressed parts from the above materials.

Processing:

1. The substrate must derusted, defatted, dry, dust-free and easy angerauht be. Altlackierung not cured or thermoplastic acrylic paint must be removed.

2. To a quantity of 100g spatula are 1-4 g hardener admitted red paste (1 g or approximately 4-5 cm from the Schraubtube).

3. Both Kompnenten until blend until a homogeneous color is reached. The mixture remains 2-6 minutes for processing.

4. After 15-30 minutes, the hardened filler edited (sanding, drilling, milling).

5. Heat accelerates, cold hardening delayed.

6. The filler surface can be edited with any commercially available fillers and coatings to be revised.

7. Devices can work with nitro-dilution cleaned.

Storage:

12 months from the date of production in unopened packaging in cooler (5 degrees C to 25 º C) and dry storage. Dawn cans well sealed and consume the short term.

Delivery:

Dose including Häter (12 doses. Per carton)